What are the main causes of zinc layer shedding?

Email：info@zhishangsteel.com

Tel：+86-13964085002

Whatsapp:+86-13964085002

Phone：+86-531-88752665

Message

The main reasons for zinc layer shedding are: Surface oxidation, silicon compounds, cold bound emulsion is too dirty, NOF section oxidation atmosphere and protective gas dew point is too high, air fuel ratio is unreasonable, hydrogen flow rate is low, furnace aerobic infiltration, strip into the pot temperature is low, RWP section furnace pressure is low and door suction, NOF section furnace temperature is low, Grease evaporation is not enough, zinc pot aluminum content is low, unit speed is too fast, insufficient reduction, zinc liquid residence time is too short, coating thickness.

Zhishang Steel has always been a pioneer in custom steel and special supplies, and has been recognized for its efforts in enhancing work efficiency and product quality. In addition to ISO9001:2015 certification, we also adhere to strict quality policies and proprietary procedures. If you have any questions, please contact us to provide the best type of product solution for your pre-painted, coil coating metal process, we will closely support after-sales service to ensure that your subsequent problems can be solved in a timely manner, if you have any questions, please send email to info@zhishangsteel.com, we look forward to serving you.